TL, OSL, EPR, and defect centers in Tb-doped strontium silicate phosphor synthesized by a solid-state reaction method

Lopez-Flores B.J.; Gundu Rao T.K.; Turpo-Huahuasoncco K.V.; Mosqueira-Yauri J.; Ayala-Arenas J.S.; Benavente J.F.; Rocca R.R.; Cano N.F. · Journal of Luminescence (2023) · DOI: 10.1016/j.jlumin.2023.120181

Resumen

Strong thermoluminescence (TL) was observed in Tb-doped strontium silicate phosphor prepared by the solid-state reaction method. Two glow peaks are observed at 100 and 190 °C. TL emission spectra indicate three recombination centers. The number of peaks and the kinetic parameters associated with the TL glow peaks of Tb-doped Sr2SiO4 phosphor after gamma irradiation were analyzed by Tm-Tstop and deconvolution methods. A study of defect centers induced by γ-irradiation and identification of defect centers responsible for the observed TL glow peaks has been carried out using the electron paramagnetic resonance (EPR) technique. The observed spectrum at room temperature is a superposition of at least three defect centers. Center I is characterized by an axially symmetric g-tensor with principal values g|| = 2.019, and g⊥ = 2.0013 and is ascribed to a O2− ion. Center II has a rhombic g-tensor with principal values 2.0072, 2.0024, and 1.995 and is assigned to an F+ center (singly ionized oxygen vacancy) and correlates with the 190 °C TL peak. The third center (center III) has an isotropic g-value of 1.991 and is identified as an F+ center.

Instituciones: Universidad Nacional de San Agustín de Arequipa